標題: | Long-term in vitro degradation and in vivo evaluation of resorbable bioceramics | 作者: | Chen Y.-C Hsu P.-Y Tuan W.-H Chen C.-Y Wu C.-J Lai P.-L. WEI-HSING TUAN |
關鍵字: | Bioceramics; Biodegradation; Bone; Calcium compounds; Defects; Degradation; Sintering; Sulfur compounds; Calcium sulfate; Degradation rate; Degradation test; Distal femurs; Initial weights; Phosphate-buffered solutions; Recovery time; Strong dependences; Strontium compounds; bioceramics; calcium sulfate; phosphate buffered saline; strontium; animal experiment; animal model; animal tissue; Article; body weight change; body weight loss; bone defect; controlled study; degradation; distal femur; fracture healing; histology; in vitro study; in vivo study; micro-computed tomography; nonhuman; priority journal; rat; X ray diffraction | 公開日期: | 2021 | 卷: | 32 | 期: | 1 | 來源出版物: | Journal of Materials Science: Materials in Medicine | 摘要: | An essential criterion for the selection of resorbable bioceramics is their ability to degrade inside human body within a reasonable time frame. Furthermore, if the bioceramic can release beneficial ions, such as strontium, as it degrades, recovery time might be shortened. The present study demonstrates that strontium-containing calcium sulfate (Sr,Ca)SO4 can fulfill these criteria. A long-term in vitro degradation analysis for 12 weeks using sintered (Sr,Ca)SO4 discs in phosphate buffered solution (PBS) was conducted. The sintered (Sr,Ca)SO4 disc was then implanted into defects in the distal femur of rats. The degradation rate of (Sr,Ca)SO4 discs showed a strong dependence on the Sr content. Similar results were observed between the long-term in vitro degradation analysis and the in vivo evaluation. The sintered (3.8%Sr,Ca)SO4 disc lost more than 80% of its initial weight after soaking in PBS with shaking at 37 °C for 12 weeks. After 12 weeks in vivo, the remaining volume of the (3.8%Sr,Ca)SO4 disc within the bone defect was ~25%. Over the same time period, new bone was formed at a relative volume of 40%. This study demonstrates the potential of (Sr,Ca)SO4 bioceramic, and the benefits of using a long-term degradation test during the evaluation of resorbable bioceramics. ? 2021, The Author(s). |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85099501862&doi=10.1007%2fs10856-020-06488-1&partnerID=40&md5=007d4a55b82bc8f71a6c5d698a18dcee https://scholars.lib.ntu.edu.tw/handle/123456789/576957 |
ISSN: | 9574530 | DOI: | 10.1007/s10856-020-06488-1 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。