標題: | Formation and microstructural variation of cerium carbonate hydroxide prepared by the hydrothermal process | 作者: | Lu, Chung-Hsin Wang, Hsien-Cheng |
關鍵字: | Cerium carbonate hydroxide;Hydrothermal process;Microstructural variation | 公開日期: | 2002 | 出版社: | Taipei:National Taiwan University Dept Chem Engn | 期: | 90 | 起(迄)頁: | 138-141 | 來源出版物: | Materials Science and Engineering B | 摘要: | Crystallized cerium carbonate hydroxide (CeCO3OH) powders have been fabricated successfully via a newly developed hydrothermal process. Comparing with the traditional precipitation method, the reaction time for synthesizing CeCO3OH under the hydrothermal condition is remarkably shortened. The hydrothermally derived CeCO3OH powders exhibit a rhombic shape with an aspect ratio of around 4–5. The aspect ratio of CeCO3OH powders increases slightly with prolonging reaction time. Based on the thermal analysis, a phase transformation from orthorhombic CeCO3OH into cubic fluorite CeO2 is confirmed to take place at around 250 °C. Fine CeO2 powders are obtained after quenching the CeCO3OH powders during heat treatment. The formation of fine CeO2 powders is attributed to the rapid decomposition reaction and resultant thermal stress in quenching treatment. |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/2006111501244001 | 其他識別: | 246246/2006111501244001 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。