標題: | Effects of pressure parameters on alumina made by powder injection moulding | 作者: | Wei, Wen-Cheng J. Wu, Rong-Yuan Ho, Sah-Jai |
關鍵字: | Al2O3; Density; Injection moulding; Sintering; Strength | 公開日期: | 2000 | 卷: | 20 | 期: | 9 | 起(迄)頁: | 1301-1310 | 來源出版物: | Journal of the European Ceramic Society | 摘要: | The effects of injection molding pressure and holding time on the properties of injection moulded (IM) parts, and the pressure-volume-temperature (PVT) relationship of the plastic ingredient and alumina feedstocks were investigated. The properties of IM parts include the mass, dimension, surface flatness, green density, sintered density and four-point bending fracture strength of the test bars. The results reveal that the pressure-time traces where the gate pressure is increased from 22 to 117 MPa and the holding time up to 75 s, illustrate the trend of the property change under these pressures. High holding pressures (≥70 MPa) and longer holding time (more than 5 s) would be favored to increase molded mass, dimension and to decrease the surface sinking of green pieces. The data also show that the pressures and holding time exert no significant influence on the bulk density of green parts, the sintered density nor the bending strength of sintered alumina. © 2000 Elsevier Science Ltd. |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/95357 https://www.scopus.com/inward/record.uri?eid=2-s2.0-0033688569&doi=10.1016%2fs0955-2219%2899%2900295-2&partnerID=40&md5=1e33a645f90874d2d59d1bbfae3bce61 |
ISSN: | 09552219 | SDG/關鍵字: | Bending strength; Ceramic materials; Density (specific gravity); Fracture toughness; Injection molding; Pressure effects; Powder injection molding; Sintered alumina |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。