標題: | 次微米級有機/無機複合乳膠顆粒之合成及性質(2/2) | 作者: | 邱文英 | 公開日期: | 2003 | 出版社: | 臺北市:國立臺灣大學材料科學與工程學研究所 | 摘要: | In this study, nano complex latex particles are prepared with Fe3O4 as core and polymer as shell. First step is to prepare a stable and well dispersed Fe3O4 suspension by using linear chain fatty acid or surfactant as surface treatment agent. the critical micelle concentration (CMC), the zeta potential, the stability and dispersity of the Fe3O4 suspension are measured under different concentration of the treatment agents. Second step is to synthesize the core-shell latex via emulsion polymerization. The influence on particle size, the polymerization rate of and the molecular weight of polymer by the kinds of monomer 、the concentration of monomer and reaction condition are studied. Finally, from the experimental results, the mechanisms of nucleation for different monomer/ Fe3O4 systems are proposed. 研究擬製備以Fe3O4 為核,高分子為殼之Fe3O4 /高分子 複合乳膠顆粒,目標粒徑大小約為數十∼100nm,為奈米級複合材料。 第一步製備安定且分散性良好的Fe3O4 懸浮液,以有機酸、介面活性劑等,作為Fe3O4 的表面處理劑,並探討處理劑的種類、處理劑的濃度、及Fe3O4 的含量,對於Fe3O4 懸浮液的CMC 值、Fe3O4 的表面電位、Fe3O4 懸浮液的安定性與分散性之影響。 第二步加入有機單體於懸浮液中,加入起始劑進行乳化聚合反應合成核-殼型乳膠顆粒,探討單體種類、含量、反應條件等對於 顆粒型態大小、包覆均勻性,單體反應速率及聚合分子量等影響;綜合以上結果,探討不同的單體/Fe3O4 系統中成核機制。 |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/12434 | 其他識別: | 912216E002020 | Rights: | 國立臺灣大學材料科學與工程學研究所 |
顯示於: | 材料科學與工程學系 |
檔案 | 描述 | 大小 | 格式 | |
---|---|---|---|---|
912216E002020.pdf | 163.98 kB | Adobe PDF | 檢視/開啟 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。