標題: | Infrared brazing of Ti-6Al-4V and 17-4 PH stainless steel with a nickel barrier layer | 作者: | Shiue, R. K. Wu, S. K. Chan, C. H. Huang, C. S. ShiueRK WuSK |
公開日期: | 2006 | 卷: | 37 | 期: | 7 | 起(迄)頁: | 2207-2217 | 來源出版物: | Metallurgical and Materials Transactions A | 摘要: | Infrared brazing of Ti-6A1-4V and 17-4 PH stainless steel using the BAg-8 filler metal was performed in this study. A nickel barrier layer 10 μm thick was introduced on the 17-4 PH stainless steel before infrared brazing. For the specimen that was infrared brazed at 800 °C and 850 °C for less than 300 seconds, the Ni layer served as an effective barrier layer to prevent the formation of Ti-Fe intermetallics. Experimental results show that the average shear strength of the joint can be greatly improved for the specimen by Ni plating. Comparing the specimens with and without electroless-plated Ni film, the former has no Ti-Fe intermetallic compound, but interfacial CuNiTi and NiPTi phases are observed in the latter. The fractured location of the joint after the shear test is changed from the interfacial TiFe (without Ni plating) into the TiCu reaction layer (with Ni plating). The plated Ni layer is consumed for the specimen that was infrared brazed at 880 °C for 300 seconds, and its bonding strength is impaired. Consequently, a lower brazing temperature and/or time are still preferred even though a plated Ni barrier layer is applied. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-33745935573&doi=10.1007%2fBF02586140&partnerID=40&md5=e85425dbff167d6260425ebf1ee77f08 http://ntur.lib.ntu.edu.tw//handle/246246/95577 |
ISSN: | 10735623 | SDG/關鍵字: | Bond strength (materials); Brazing; Electroless plating; Filler metals; Intermetallics; Nickel; Shear strength; Thermal barrier coatings; Infrared brazing; Nickel barrier layer; Stainless steel |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。