標題: | Focused-Ion-Beam-Based Selective Closing and Opening of Anodic Alumina Nanochannels for the Growth of Nanowire Arrays Comprising Multiple Elements | 作者: | Liu, Nai-Wei Liu, Chih-Yi Wang, Huai-Hsien Hsu, Chen-Feng Lai, Ming-Yu Chuang, Tung-Han Wang, Yuh-Lin |
公開日期: | 2008 | 卷: | 20 | 期: | 13 | 起(迄)頁: | 2547-2551 | 來源出版物: | Advanced Materials | 摘要: | The development of a complete resist-free lithographic process for the selective closing and reopening of anodic aluminum oxide (AAO) nanochannels, using focused ion beam (FIB) direct writing, was reported. The image analysis results indicate that the average pore diameter of an ordered array gradually decreases with increasing ion dose, whereas standard deviation of the pore diameter increases with increasing ion dose. The reduction in pore diameter is found to be strongly dependent on the energy of the FIB, while the changes in the surface morphology is due to large size variations of the pores. The results also show that the materials within the simulated range are relocated by ion bombardment to maintain the equilibrium thickness of the capping layer. The growth of Ag nanowires takes place within the open nanochannels, and no deposition of Ag is found to occur in the closed nanochannels. |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/95972 https://www.scopus.com/inward/record.uri?eid=2-s2.0-54949155526&doi=10.1002%2fadma.200702604&partnerID=40&md5=7c7e4acb09b2ed49816f686b65b10d50 |
ISSN: | 09359648 | SDG/關鍵字: | Alumina; Electric wire; Focused ion beams; Image analysis; Ion beams; Ions; Nanostructured materials; Nanostructures; Nanowires; Water pollution; Ag nanowires; Analysis results; Anodic aluminas; Anodic aluminum oxides; Capping layers; Direct writings; Ion doses; Large sizes; Lithographic processes; Multiple elements; Nanochannels; Nanowire arrays; Ordered arrays; Pore diameters; Standard deviations; Ion bombardment |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。