標題: | Preparation and in vivo evaluation of a newly developed bioglass ceramic | 作者: | Lin, Feng-Huei Liu, Haw-Chang Hon, Ming-Hsiung Wang, Cheng-Yi LinFengHuei |
關鍵字: | Bioglass ceramic; bone graft; nucleation | 公開日期: | 1993 | 卷: | 15 | 期: | 6 | 起(迄)頁: | 481-486 | 來源出版物: | Journal of Biomedical Engineering | 摘要: | This paper presents details of the fabrication of a glass ceramic, and its application as an artificial bone prosthetic material. This new bioglass ceramic, with composition of Na2O 8.4%, CaO 40.6%, P2O5 12% and SiO2 39%, had 160-190 MPa and 800-980 MPa of three-point bending strength and compressive strength respectively. The ceramic has a (Na, Ca) (P, Si) O3 crystalline phase with a uniform crystal size of about 10μm, which was attributed to the high nucleation frequency. The rabbit condyle test showed that the material formed a tight chemical bond with biological texture and had good biocompatibility. © 1993. |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/127967 https://www.scopus.com/inward/record.uri?eid=2-s2.0-0027703496&doi=10.1016%2f0141-5425%2893%2990063-5&partnerID=40&md5=c57973b468a3bce685f1beaaace807ba |
ISSN: | 01415425 | SDG/關鍵字: | Biocompatibility; Biomedical engineering; Bone; Ceramic materials; Glass; Grafts; Implants (surgical); Mechanical properties; Prosthetics; Bioglass ceramic; Compressive strength; In vivo evaluation; Nucleation frequency; Rabbit condyle test; Biomaterials; animal experiment; article; biocompatibility; bone graft; ceramics; nonhuman; priority journal; rabbit; Animal; Biocompatible Materials; Biomechanics; Ceramics; Evaluation Studies; Femur; Materials Testing; Osseointegration; Prostheses and Implants; Rabbits; X-Ray Diffraction; Animalia; Oryctolagus cuniculus |
顯示於: | 醫學工程學研究所 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。