Yu-Ming JaoBo-Ming HuangChing ChangFang-Zhong LinGuan-Ying LeeChung-Ping HuangHao-Chung KuoMin-Hsiung ShihChien-Chung Lin2024-08-132024-08-132024-05-27https://scholars.lib.ntu.edu.tw/handle/123456789/720226<jats:p>A special micro LED whose light emitting area is laid out in a U-like shape is fabricated and integrated with colloidal quantum dots (CQDs). An inkjet-type machine directly dispenses the CQD layer to the central courtyard-like area of this U-shape micro LED. The blue photons emitted by the U-shape mesa with InGaN/GaN quantum wells can excite the CQDs at the central courtyard area and be converted into green or red ones. The U-shape micro LEDs are coated with Al2O3 by an atomic layer deposition system and exhibit moderate external quantum efficiency (6.51% max.) and high surface recombination because of their long peripheries. Low-temperature measurement also confirms the recovery of the external quantum efficiency due to lower non-radiative recombination from the exposed surfaces. The color conversion efficiency brought by the CQD layer can be as high as 33.90%. A further continuous CQD aging test, which was evaluated by the strength of the CQD emission, under current densities of 100 A/cm2 and 200 A/cm2 injected into the micro LED, showed a lifetime extension of the unprotected CQD emission up to 1321 min in the U-shape device compared to a 39 min lifetime in the traditional case, where the same CQD layer was placed on the top surface of a squared LED.</jats:p>[SDGs]SDG7journal article10.3390/nano14110938