標題: | Rapid Thermal Post-Metallization Annealing Effect on the Reliability of Thin Gate Oxides | 作者: | 胡振國 Jeng, M. J. Lin, H. S. |
關鍵字: | Breakdown characteristics; Metal-oxide-semiconductor; Postmetallization annealing; Rapid thermal; Thin gate oxides | 公開日期: | 1994 | 摘要: | Rapid thermal technique was used in the post-metallization annealing (PMA) of thin gate oxide devices. A suitable choice of the rise rate, the setting temperature, and the hold time in the rapid thermal PMA (RTPMA) process is helpful to improve the oxide quality. It was found that the samples subjected to appropriate RTPMA conditions exhibit almost the same initial characteristic in flatband voltage Vfb and midgap interface trap density Atm as those subjected to conventional furnace PMA (FPMA). However, the RTPMA samples exhibit longer time-to- breakdown £bd and higher time-zero-dielectric-breakdown (TZDB) field Ebd than the FPMA ones. In addition to the known spiking effect caused by aluminum penetration into silicon, which seriously degrades the breakdown property, formation of aluminum oxide near the AI/S1O2 interface in the early stage and then aluminum silicon alloy in the later stage was proposed to explain the experimental observation. © 1995 The Japan Society of Applied Physics. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-0029404955&doi=10.1143%2fJJAP.34.6008&partnerID=40&md5=47ded0ea4daefa9b5d8d2afee5043e8a | DOI: | 10.1143/JJAP.34.6008 | SDG/關鍵字: | Aluminum alloys; Aluminum compounds; Annealing; Electric breakdown; Electric conductivity; Electric fields; Interfaces (materials); Oxides; Silicon wafers; Flatband voltage; Midgap interface trap density; Postmetallization annealing; Rapid thermal annealing; Thin gate oxides; MOS devices |
顯示於: | 電機工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。