標題: | Enhanced performance of dye-sensitized solar cell with thermally-treated TiN in its TiO2 film prepared at low temperature | 作者: | Lee, C.-P. Lin, L.-Y. Tsai, K.-W. Vittal, R. Ho, K.-C. KUO-CHUAN HO |
關鍵字: | Binder-free titanium dioxide; Dye-sensitized solar cell; Electron lifetime; Low temperature process; Thermally-treated titanium nitride | 公開日期: | 2011 | 卷: | 196 | 期: | 3 | 起(迄)頁: | 1632-1638 | 來源出版物: | Journal of Power Sources | 摘要: | Various weight percentages of titanium nitride (TiN) and thermally-treated titanium nitride (tt-TiN) are incorporated into the binder-free TiO2 films, prepared at low temperature (LT, 120 °C), and the corresponding dye-sensitized solar cells (DSSCs) are made. Effects of their incorporation on the photovoltaics of the DSSCs are studied. With the incorporation of 0.125 wt% of TiN in a TiO2 film of only 5.5 μm-thickness, the corresponding solar-to-electricity conversion efficiency (η) has reached to 3.40% from 2.38% of a cell with a bare TiO2 film of same thickness; this increase in efficiency is attributed to the higher electron conductivity and longer electron life time in the TiO2 film with TiN. Incorporation of 1.0 wt% of tt-TiN into the TiO2 film has further improved the conversion efficiency to 3.77%; this further enhancement in the efficiency is attributed to the partial conversion of TiN into TiO2 due to the thermal treatment (450 °C). X-ray diffraction (XRD) and scanning electron microscopy (SEM) are used to study the partial conversion of TiN into TiO 2. Other explanations are supported by the data of UV-absorption spectra, electrochemical impedance spectroscopy (EIS), and laser-induced photo-voltage transients. © 2010 Elsevier B.V. |
URI: | http://www.scopus.com/inward/record.url?eid=2-s2.0-78049385152&partnerID=MN8TOARS http://scholars.lib.ntu.edu.tw/handle/123456789/363186 |
DOI: | 10.1016/j.jpowsour.2010.09.022 | SDG/關鍵字: | Dye-sensitized solar cell; Dye-sensitized solar cells; Electron conductivity; Electron lifetime; Enhanced performance; Laser induced; Life-times; Low temperatures; Low-temperature process; Photo-voltage; Photovoltaics; SEM; Thermal treatment; Thermally-treated titanium nitride; TiO; Weight percentages; Absorption spectroscopy; Binders; Conversion efficiency; Electrochemical corrosion; Electrochemical impedance spectroscopy; Electrons; Film preparation; Oxides; Photoelectrochemical cells; Scanning electron microscopy; Solar cells; Titanium; Titanium dioxide; Transients; X ray diffraction; Titanium nitride |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。