Ag-modified TiO2/SiO2/Fe3O4 sphere with core-shell structure for photo-assisted reduction of 4-nitrophenol

Nitrogen-containing contaminants, such as 4-nitrophenol (4-NP), cause detrimental effects when discharged into the environment and thus should be reduced or removed from ecosystems. In this study, an Ag-loaded TiO2–SiO2–Fe3O4 (TSF) with a core-shell structure was employed for the photo-assisted reduction of 4-NP. Fe3O4, SiO2, and TiO2 in the core-shell structure served as a magnetic center, protective layer, and light absorber, respectively. To improve the reduction activity of 4-NP, Ag was loaded onto TSF under stirring, with a variation of the temperature (2–130 °C) and reaction time (1, 2, and 4 h). Under the optimized conditions, 5Ag-TSF (with 5 wt% of Ag) could promote the reduction of aqueous 4-NP solution (2 × 10−4 M, 75 mL) in the presence of NaBH4 (0.1 M, 5 mL) under irradiation by a metal halide lamp, affording over 98% reduction within 5 min and a rate constant of 0.185 min−1, demonstrating its promising activity. Moreover, due to the advantages of the core-shell structure, the magnetic properties of Fe3O4 were sufficient to enable facile recycling of the sample for further reaction; SiO2 could protect the Fe3O4 center from oxidation or reduction; TiO2 enabled Ag accommodation and absorbed light to generate electron-hole pairs. In summary, an Ag-loaded TiO2–SiO2–Fe3O4 sphere with high activity and recyclability for 4-NP reduction was prepared via a facile and simple stirring method, where the sample can be used as a promising material in environmental remediation.