標題: | All-Solid-State Li-Ion Battery Using Li1.5Al0.5Ge1.5(PO4)3 As Electrolyte Without Polymer Interfacial Adhesion | 作者: | Yedukondalu Meesala Chen-Yu Chen Anirudha Jena Yu-Kai Liao Shu-Fen Hu Ho Chang RU-SHI LIU |
公開日期: | 2018 | 出版社: | American Chemical Society ({ACS}) | 來源出版物: | The Journal of Physical Chemistry C | 摘要: | Solid-state lithium-ion batteries are promising candidates for energy storage devices that meet the requirements to reduce CO2 emissions. NASICON-type solid-state electrolytes (SSE) are most promising materials as electrolytes for high-performance lithium ion batteries because of their good stability and high ionic conductivity. In this study, we successfully fabricate NASICON-based Li1.5Al0.5Ge1.5(PO4)3 lithium fast-ion conductors through melt-quenching with post-crystallization. The effect of crystallization temperature on the structure of LAGP and their ionic conductivity is systematically studied using Rietveld analysis of Synchrotron X-ray powder diffraction patterns, multinuclear magnetic resonance, and electrochemical analysis, revealing that the mobility of Li ion is dependent on crystallization temperature. The glass-ceramic LAGP annealed at 800 °C for 8 h exhibits the highest conductivity of 0.5 mS cm-1 at room temperature. Moreover, we report the viability of the prepared LAGP glass-ceramic as a solid electrolyte in Li-ion batteries without polymer adhesion. The cycling of Li/LAGP/LFP all-solid-state cell, provides a stable cycling lifetime of up to 50 cycles. This approach demonstrates that LAGP glass-ceramic can have good contact with the electrodes without interfacial layer and can deliver a reasonable discharge capacity after 50 cycles. © 2018 American Chemical Society. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/403266 | DOI: | 10.1021/acs.jpcc.8b03971 | SDG/關鍵字: | Adhesion; Aluminum compounds; Electric discharges; Germanium compounds; Glass ceramics; Ionic conduction in solids; Ionic conductivity; Ions; Lithium compounds; Lithium-ion batteries; Rietveld analysis; X ray powder diffraction; Crystallization temperature; Discharge capacities; Electrochemical analysis; High-performance lithium-ion batteries; Interfacial adhesions; Solid state lithium ion battery; Solid-state electrolyte; Synchrotron X ray powder diffraction; Solid electrolytes |
顯示於: | 化學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。