https://scholars.lib.ntu.edu.tw/handle/123456789/407348
標題: | Photoluminescence and cathodoluminescence properties of green¡Vred emitting ZnGd4Si3O13: Tb3+, Mn2+ phosphors | 作者: | Yang C.-Y. Som S. Das S. Lu C.-H. |
公開日期: | 2017 | 卷: | 28 | 期: | 12 | 起(迄)頁: | 9174-9181 | 來源出版物: | Journal of Materials Science: Materials in Electronics | 摘要: | The photoluminescence and cathodoluminescence properties of new silicate oxyapatite phosphors ZnGd4Si3O13: Tb3+, Mn2+ were investigated in this study. The Rietveld refinement indicated that the prepared phosphors exhibited a hexagonal structure with space group P63/m (no. 176). Under UV excitation, ZnGd4Si3O13: Mn2+ phosphors presented a red emission band due to the T1(4G)¡V6A1(6S) transition of Mn2+ ions, while ZnGd4Si3O13: Tb3+ showed several emission lines at 490, 544, 585 and 621?nm attributed to the 5D4¡÷7FJ (J = 6, 5, 4, 3) transitions of Tb3+ ions. The co-doping of Tb3+ ions into ZnGd4Si3O13: Mn2+ resulted in a 100% enhancement of the photoluminescence intensity for Mn2+ ions through a dipole¡Vdipole energy transfer mechanism. On the other hand, the energy transfer process from the sensitizers (Tb3+) to the activators (Mn2+) led to a decrease in Tb3+ emission as co-doping Mn2+ ions into ZnGd4Si3O13: Tb3+. Increasing the concentration of Mn2+ ions from x = 0.02 to x = 0.08 for Zn2?xMnxGd3TbSi3O13 efficiently enhanced the energy transfer efficiency from 90 to 98%. Under the electron-beam excitation, the emission spectra of phosphors were similar to those observed under UV excitation. However, a deviation of CIE coordinates was found under the electron-beam excitation due to the relatively unapparent energy transfer between Tb3+ and Mn2+ ions. The present results suggested a new series of color-tunable phosphors which can be used for both photoluminescence and cathodoluminescence applications. ? 2017, Springer Science+Business Media New York. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/407348 | ISSN: | 09574522 | DOI: | 10.1007/s10854-017-6651-x |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。