標題: | Low-temperature synthesis of Cu (In, Ga) Se 2 thin films using selenium-containing precursors | 作者: | Chen F.-S. Wu C.-H. Lu C.-H. |
公開日期: | 2012 | 卷: | 9 | 期: | 4 | 起(迄)頁: | 853-860 | 來源出版物: | International Journal of Applied Ceramic Technology | 摘要: | Cu(In,Ga)Se 2 films were successfully synthesized via employing H 2 SeO 3 as a new Se source. Direct heating in a reducing atmosphere at 350¢XC without using Se vapor yielded monophasic Cu(In,Ga)Se 2. H 2SeO 3 was completely dissolved in the starting solution, leading to an improvement in homogeneous mixing and diffusion of selenium atoms with other constituent species in the precursor pastes. The formation processes of Cu(In,Ga)Se 2 were investigated, and the related reaction mechanism was proposed in the study. H 2SeO 3 is first decomposed to yield selenium species at elevated temperatures. Subsequently, In 2Se 3 is formed from selenium and indium species. Finally, In 2Se 3 reacts with other species to yield Cu(In,Ga)Se 2. In the heating process, decreasing the heating rates resulted in a significant increase in the grain size and the compactness of the prepared films. ? 2012 The American Ceramic Society. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/407395 | ISSN: | 1546542X | DOI: | 10.1111/j.1744-7402.2012.02777.x |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。