標題: | Effects of current collectors on power performance of Li 4Ti 5O 12 anode for Li-ion battery | 作者: | Wu H.-C. Lee E. Wu N.-L. |
關鍵字: | Aluminum;Carbon coating;Copper;Current collector;Lithium titanate anode;Lithium-ion battery | 公開日期: | 2012 | 卷: | 197 | 起(迄)頁: | 301-304 | 來源出版物: | Journal of Power Sources | 摘要: | The effects of current collector on the charge/discharge capacity and cycle stability of Li 4Ti 5O 12 (LTO) electrode under high C-rates (up to 20 C) have been investigated by applying five types of current collectors, including a Al foil, an anodization-etched Al (E-Al), the same etched Al with a conformal C coating (C-E-Al), a Cu foil (Cu) and the same Cu foil with a C coating (C-Cu). The C coatings on both metal current collectors are deposited by a chemical vapor deposition process using CH 4 at 600 ¢XC. The capacities of the LTO electrodes above 1 C rate are in the order of Al < E-Al < Cu ? C-E-Al < C-Cu, exhibiting remarkable enhancement in rate performance by the C-coating for both metals. Surface analyses indicate that the enhancement can be attributed to the combination of two factors, including removal of the native oxide layer and modification of surface hydrophobicity, which improves adhesion of active layer, on the current collector surface. Both contribute to the reduction of the resistance at the current-collector/active layer interface. All electrodes show good cycle stability. ? 2011 Elsevier B.V. All rights reserved. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/408515 | ISSN: | 03787753 | DOI: | 10.1016/j.jpowsour.2011.09.014 | SDG/關鍵字: | Active Layer; Al foil; Carbon coating; Charge/discharge; Chemical vapor deposition process; Cu foil; Current collector; Cycle stability; Layer interfaces; Li-ion batteries; Lithium titanate anode; Lithium-ion battery; Native oxide layer; Power performance; Rate performance; Surface hydrophobicity; Aluminum; Aluminum coatings; Aluminum foil; Chemical vapor deposition; Coatings; Electric current collectors; Electrodes; Lithium; Metal cladding; Secondary batteries; Power quality |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。