標題: | Solution-growth-synthesized Cu(In,Ga)Se2 nanoparticles in ethanol bath for the applications of dye-sensitized solar cell and photoelectrochemical reaction | 作者: | Cheng K.-W. Jhang H.-J. Li C.-T. Ho K.-C. |
關鍵字: | Counter electrode;CuIn1 ? xGaxSe2 (CIGSe);Dye-sensitized solar cells (DSSCs);Photoelectrochemical reaction | 公開日期: | 2017 | 卷: | 74 | 起(迄)頁: | 136-145 | 來源出版物: | Journal of the Taiwan Institute of Chemical Engineers | 摘要: | In this study, ternary CuInSe2 and quaternary CuIn1 ? xGaxSe2 (CIGSe) nanoparticles (NPs) are grown in the ethanol bath using the one step solution growth method. The influence of Ga content in samples on the optical and electronic properties of the samples is investigated. Average particle sizes of samples are less than 66?nm after a 10-min. reaction in the solution. The NPs are prepared as the ink for the deposition of CIGSe samples on substrates. X-ray diffraction patterns of samples reveal that samples are the chalcopyrite CIGSe phase when the [Ga]/[In+Ga] molar ratio in solution bath of less than 0.5. The carrier concentration and mobility of samples are in the ranges of 1.2?¡Ñ?1013?9.1?¡Ñ?1015?cm?3 and 1.4¡V205?cm2/V/s, respectively. The results show that the maximum photo-conversion efficiency of 7.02% for the dye-sensitized solar cells using CIGSe as the counter electrodes and the maximum photoelectrochemical performances of 0.96?mA/cm2 at an external bias of ?0.8?V vs. an Ag/AgCl electrode using the CIGSe as the photoelectrodes in salt¡Vwater solution, respectively. ? 2017 Taiwan Institute of Chemical Engineers |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/408647 | ISSN: | 18761070 | DOI: | 10.1016/j.jtice.2017.02.010 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。