標題: | Determination of mass transfer resistance during absorption of carbon dioxide by mixed absorbents in PVDF and PP membrane contactor | 作者: | Lin S.-H. Hsieh C.-F. Li M.-H. Tung K.-L. |
關鍵字: | Absorption;CO2;Mass transfer resistance;Microporous hollow fiber;Mixed absorbent | 公開日期: | 2009 | 卷: | 249 | 期: | 2 | 起(迄)頁: | 647-653 | 來源出版物: | Desalination | 摘要: | In this study, the absorption of carbon dioxide by the absorbent which was composed of 2-amino-2-methyl-l-propanol (AMP) + piperazine (PZ) or methyldiethanolamine (MDEA) + piperazine (PZ) in polyvinylidinefluoride (PVDF) and polypropylene (PP) membrane contactors werewas examined. Three resistances were considered in each hollow fiber, i.e., liquid-film diffusion, membrane diffusion, and gas-film diffusion. The mass transfer resistance of membrane km was influenced by the wetting ratio using an absorbent with higher reaction rate. The wetting ratio was affected by contact angle between the membrane and absorbent and the viscosity of absorbent. The calculated absorption rates considering wetting ratio of membrane and using the modified correlation equation of gas-phase mass transfer coefficient were reasonably agreeable to those of measured ones (standard deviation, 4%). The fractional resistance of each transport step during the experiments was then determined. The rate-controlling step was dominated by the resistance of gas-film diffusion with mixed absorbents. The absorption rates of CO2 increase with the increasing of gas flow rates in the most experimental cases. The resistance of liquid-film diffusion was only important using an absorbent with lower reaction rate. The rate-controlling step was the membrane diffusion only at higher gas flow rate with the absorbent composed of AMP and PZ in PVDF hollow fiber membrane contactor. ? 2009 Elsevier B.V. All rights reserved. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/410485 | ISSN: | 00119164 | DOI: | 10.1016/j.desal.2008.08.019 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。