標題: | Nanoscaled superelastic behavior of shape memory alloy/metallic glass multilayered films | 作者: | Jhou W.T. Wang C. Ii S. Hsueh C.H. CHUN-HWAY HSUEH |
關鍵字: | Layered structures;Microstructures;Stress-induced martensitic transformation;Thin films | 公開日期: | 2018 | 卷: | 142 | 起(迄)頁: | 193-199 | 來源出版物: | Composites Part B: Engineering | 摘要: | The mechanical properties of multilayered films with alternate layers of shape memory alloy (SMA) and metallic glass (MG) were studied. Specifically, TiNi SMA and ZrCuAlNi MG were deposited alternately on the Si substrate using magnetron sputtering. The as-deposited multilayered film was amorphous. The annealing temperature was chosen judiciously to crystalize TiNi layer while ZrCuAlNi layer remained amorphous. The superelastic behavior of SMA/MG multilayered film was characterized using nanoindentation tests. The stress required to induce martensitic transformation of TiNi layer increased as the thickness of TiNi layer decreased. Also, the multilayered SMA/MG films were found to have the better deformation recovery after indentation unloading which could be due to the synergy effects of superelasticity from SMA layers and high elastic strain limit from MG layers. ? 2018 Elsevier Ltd |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/425002 | ISSN: | 13598368 | DOI: | 10.1016/j.compositesb.2018.01.029 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。