標題: | Resource Recoveiy of Waste Fly Ash: Synthesis of Zeolite-like Materials | 作者: | CHENG-FANG LIN HSING-CHENG HSI |
公開日期: | 1-一月-1995 | 卷: | 29 | 期: | 4 | 起(迄)頁: | 1109 | 來源出版物: | Environmental Science and Technology | 摘要: | Since the main components of fly ash are SiO2 and Al2O3, which exhibit a similar chemical structure of zeolite, fly ash was used in this study to synthesize zeolite-like materials. Different hydrothermal conditions were evaluated for achieving a maximum cationexchange capacity of the synthesized zeolites. Experimental parameters included temperature, nature and molarity of caustic reagents, pressure, and reaction time. Tasks performed in this work included phase identification of treated fly ash by X-ray diffraction techniques, measurement of cation-exchange capacity and specific surface area of the synthesized zeolites, determination of elemental composition, and evaluation of metal adsorption onto the synthesized zeolites. Four zeolites were identified under various experimental conditions: zeolite P (2-4 N NaOH at 70-130 °C); analcime (2 N NaOH between 130 and 170 °C); hydroxy sodalite (4-10 N NaOH at 90-200 °C); and cancrinite (T > 200 °C). After NaOH treatment, there was a significant reduction in Si content, while Na increased as the reaction temperature or the strength of NaOH increased. The experimental conditions at 2 N NaOH, 110 °C, and 3.45 MPa for 1-day reaction resulted in treated fly ash with a cationexchange capacity of 210 mequiv/100 g. Treated fly ash exhibited a strong affinity for Cu and Cd metal ions. At pH = 6, approximately 90% of Cu and 80% of Cd were removed by the zeolites synthesized under different conditions. © 1995, American Chemical Society. All rights reserved. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/425178 | ISSN: | 0013936X | DOI: | https://api.elsevier.com/content/abstract/scopus_id/0029278211 10.1021/es00004a033 |
顯示於: | 環境工程學研究所 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。