Effective passivation of In 0.2Ga 0.8As by HfO 2 surpassing Al 2O 3 via in-situ atomic layer deposition
Journal
Applied Physics Letters
Journal Volume
101
Journal Issue
17
Date Issued
2012
Author(s)
Abstract
High κ gate dielectrics of HfO2 and Al2O3 were deposited on molecular beam epitaxy-grown In0.2Ga0.8As pristine surface using in-situ atomic-layer-deposition (ALD) without any surface treatment or passivation layer. The ALD-HfO2/p-In0.2Ga0.8As interface showed notable reduction in the interfacial density of states (Dit), deduced from quasi-static capacitance-voltage and conductance-voltage (G-V) at room temperature and 100 °C. More significantly, the midgap peak commonly observed in the Dit(E) of ALD-oxides/In0.2Ga0.8As is now greatly diminished. The midgap Dit value decreases from ≥15 × 1012 eV−1 cm−2 for ALD-Al2O3 to ∼2–4 × 1012 eV−1 cm−2 for ALD-HfO2. Further, thermal stability at 850 °C was achieved in the HfO2/In0.2Ga0.8As, whereas C-V characteristics of Al2O3/p-In0.2Ga0.8As degraded after the high temperature annealing. From in-situ x-ray photoelectron spectra, the AsOx, which is not the oxidized state from the native oxide, but is an induced state from adsorption of trimethylaluminum and H2O, was found at the ALD-Al2O3/In0.2Ga0.8As interface, while that was not detected at the ALD-HfO2/In0.2Ga0.8As interface.
SDGs
Type
journal article