Strengthening polymer interfaces With triblock copolymers
Journal
Macromolecules
Journal Volume
30
Journal Issue
3
Pages
549-560
Date Issued
1997
Author(s)
Abstract
We have measured the fracture toughness, Gc, of an interface between polystyrene (PS) and poly (2-vinylpyridine) (PVP) reinforced with triblock copolymers (PVP-b-dPS-b-PVP) as a function of the areal chain density, Σ, of the copolymers at the interface. The failure mechanisms of the interface are studied by transmission electron microscopy and forward recoil spectrometry. For triblock copolymers with long PVP blocks (NPVP > NePVP, where NePVP is the entanglement polymerization index of PVP), a transition from chain scission at low Σ to crazing at high Σ* is observed. By comparing the areal chain density Σ* for the transition from chain scission to crazing for the triblock copolymers (Σ* = 0.015 chains/ nm2) to that for the diblock copolymers, PVP-dPS (Σ* = 0.03 chains/nm2), we show that most of the triblock copolymers form a "staple" structure at the interface with the dPS block making a loop on the PS side of the interface and the PVP ends anchoring the "staple" in the PVP side. As a result of the "staple" structure, the saturation areal chain density of the triblock copolymer (Σsat) at the interface is half of that for the diblock copolymer of similar molecular weight. For Σ< Σsat in the crazing regime, the fracture toughness of the interface is controlled by the areal joint density, Σcross, where Σcross is the number density of the copolymer excursions across the interface. For Σ> Σsat, the triblock copolymers appear to reinforce the craze fibrils at the crack tip better than the corresponding diblock copolymers, leading to an interface fracture toughness approaching that of the PS homopolymer itself. For a triblock copolymer with short PVP blocks NPVP < NePVP), there is a transition in the fracture mechanism from pull out of the PVP block to crazing with increasing Σ. Short triblock copolymers can form two chain conformations: one in which two PVP blocks anchor the copolymer on the homopolymer PVP side (staple structure) and one in which one PVP block anchors the copolymer on the PVP side (tail structure) of the interface. Comparison of Gc between the triblock copolymer and the corresponding diblock copolymer is made. The larger Gc values of the triblock copolymer reinforced interface in the crazing regime are observed as a result of enhancement in entanglements between the dPS loops of the triblock copolymer and the homopolymer PS.
Type
journal article