Solubility of Silver and Palladium in BaTiO3
Journal
Journal of the American Ceramic Society
Journal Volume
87
Journal Issue
3
Pages
401-407
Date Issued
2004
Author(s)
Abstract
Silver, palladium, and their alloys are frequently used as electrode materials for BaTiO 3 (BT) based dielectrics. However, the electrodes and dielectrics usually are cofired at high temperatures, and silver and palladium can dissolve into the BT during cofiring. In the present study, the solubility of silver and palladium into BT after cofiring was determined. Three measurement techniques were used to determine solubility: chemical analysis, structural analysis, and dielectric analysis. The solubility of the silver in the BT was low, 450 ppm, after cofiring at 1290°C for 2 h in air. The diffusion distance of the silver ions into the BT was >5 μm. The solubility of the palladium in the BT was even lower, 50 ppm at 1290°C, and the diffusion distance was ∼1 μm. The solubility of both the silver and the palladium in the BT decreased as the oxygen partial pressure of the sintering atmosphere decreased. These results demonstrated that both silver and palladium solutes act as acceptors for BT.
Type
journal article