標題: | Porous organic polymer derived metal-free carbon composite as an electrocatalyst for CO 2 reduction and water splitting | 作者: | Rajagopal, V. Kathiresan, M. Manivel, P. Suryanarayanan, V. Velayutham, D. Ho, K.-C. KUO-CHUAN HO |
關鍵字: | Electrocarboxylation; Electrocatalysis; Porous organic polymers; Pyrolysis; Water-splitting | 公開日期: | 2020 | 卷: | 106 | 起(迄)頁: | 183-190 | 來源出版物: | Journal of the Taiwan Institute of Chemical Engineers | 摘要: | A hybrid porous organic polymer (POP) comprising of phenylenediamine, phloroglucinol and triazine was synthesized, carbonized at different temperatures and characterized. Solid state 13C and 15N CP-MAS NMR spectra of the POP showed evidences for the presence of the three moieties in varying composition. Raman analysis of the carbonized samples exhibited varying degrees of graphitization and powder X-ray diffraction (PXRD) analysis showed patterns corresponding to N-doped amorphous carbon. Surface morphological characteristics obtained from SEM and TEM analysis confirm different morphologies with slight variations in the particle size and porosity. Further, the electrocatalytic activities of the prepared metal-free catalysts were evaluated. Sample carbonized at 700 °C (PPT-700) showed excellent catalytic activity towards electrocarboxylation of 4-bromoacetophenone in 0.1 M TBABF4/DMF and OER in 1 M KOH as indicated by their onset potential and current density, whereas the sample calcined at 900 °C (PPT-900) exhibited excellent HER activity in 1 M H2SO4. The catalytic activity of PPT-700 towards electrocarboxylation and OER activity is ascribed to the presence of pyridinic, pyrrolic and quaternary nitrogen's, whereas the presence of pyridinic and pyrrolic nitrogen's are responsible for the enhanced HER activity of PPT-900 sample as evident from XPS. © 2019 Taiwan Institute of Chemical Engineers |
URI: | https://www.scopus.com/inward/record.url?eid=2-s2.0-85075482858&partnerID=40&md5=b0e2d4ca3a993326fb542fbab9bb63a4 https://scholars.lib.ntu.edu.tw/handle/123456789/546465 |
DOI: | 10.1016/j.jtice.2019.10.016 | SDG/關鍵字: | Amorphous carbon; Carbon carbon composites; Catalyst activity; Complexation; Doping (additives); Electrocatalysis; Electrocatalysts; Metal analysis; Nitrogen; Nuclear magnetic resonance spectroscopy; Particle size; Particle size analysis; Potassium hydroxide; Pyrolysis; Electrocarboxylation; Electrocatalytic activity; Metal-free catalysts; Morphological characteristic; Porous organic polymers; Powder X-ray diffraction (pXRD); Quaternary nitrogens; Water splitting; Organic polymers |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。