標題: | Strontium ion can significantly decrease enamel demineralization and prevent the enamel surface hardness loss in acidic environment | 作者: | YIN-LIN WANG HAO-HUENG CHANG YU-CHIH CHIANG Lin C.-H. CHUN-PIN LIN |
公開日期: | 2019 | 出版社: | Elsevier B.V. | 卷: | 118 | 期: | 1P1 | 起(迄)頁: | 39-49 | 來源出版物: | Journal of the Formosan Medical Association | 摘要: | Background/purpose: Strontium ion may play a role similar to calcium ion in enamel remineralization. The aim of this study was to investigate the effect of strontium ion concentration gradient on the demineralization of enamel. Methods: Citric acid and sodium citrate were used to prepare 16 different experimental acidic solutions with four different pH values (2.5, 3.5, 4.5, and 5.5) and four different strontium ion concentrations (0 M, 10 ?4 M, 10 ?3 M, and 10 ?2 M). Forty-eight human enamel samples were divided into 16 groups (n = 3) and immersed into the 16 different acidic solutions for 3 min. The phosphorus ion concentrations in 16 different acidic solutions were measured and compared. The enamel surface hardness was measured with a Vickers hardness tester. The energy dispersive spectrometer was used to detect the strontium ion content in the enamel surface. Results: Addition the strontium ions to the acidic solution could reduce the dissolution of the enamel. At pH 3.5 and pH 5.5, significantly lower phosphorus ion concentrations were detected in the acidic solutions with the addition of 10 ?2 M strontium ions. There was a less reduction of enamel surface hardness, while the strontium ion concentration increased in the acidic solution. At pH 2.5, the addition of 10 ?4 M, 10 ?3 M, or 10 ?2 M strontium ions to the acidic solution resulted in a significant increase in the strontium ion content in the enamel surface. Conclusion: Strontium ion can decrease the dissolution of the enamel and prevent the enamel surface hardness loss in acidic environment. ? 2018 |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85041559098&doi=10.1016%2fj.jfma.2018.01.001&partnerID=40&md5=7baa9119891f052bb342689b034fee54 https://scholars.lib.ntu.edu.tw/handle/123456789/570013 |
ISSN: | 0929-6646 | DOI: | 10.1016/j.jfma.2018.01.001 | SDG/關鍵字: | citrate sodium; citric acid; phosphorus; strontium; calcium; ion; phosphate; strontium; acidity; Article; demineralization; dissolution; enamel; energy dispersive X ray spectroscopy; hardness; human; surface property; chemistry; dental procedure; drug effect; enamel; pH; tooth disease; Calcium; Dental Enamel; Hardness; Humans; Hydrogen-Ion Concentration; Ions; Phosphates; Strontium; Tooth Demineralization; Tooth Remineralization |
顯示於: | 臨床牙醫學研究所 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。