Title: | Extraordinary warm ductility of a Mn-rich high-strength steel achieved at temperature below 0.5 Tm | Authors: | Cheng G.-J Lai Z.-H Jia T Huang C.-Y Yen H.-W. HUNG-WEI YEN |
Keywords: | Aluminum coated steel; Austenite; Deformation; Ductility; Manganese steel; Strain energy; Temperature; Austenite reversion; Electron back scatter diffraction; Micro-structure evolutions; Thermodynamic calculations; Warm deformation; High strength steel | Issue Date: | 2021 | Journal Volume: | 803 | Source: | Materials Science and Engineering A | Abstract: | This work employed austenite reversion during deformation to achieve large ductility at a temperature below 0.5 Tm (melting temperature) in Mn-rich high strength steels. This goal was achieved in a Mn-rich steel without Al, in which a higher austenite reversion rate below 0.5 Tm was obtained. The tensile results evidenced the extraordinary ductility of over 90% at 550 °C, which is about 0.48 Tm of the steel. Thermodynamic calculation was applied to elucidate the effects of Al and strain energy. Moreover, electron backscatter diffraction was used to investigate microstructure evolution under various conditions. It was found that rate of austenite reversion is more critical than ferrite recrystallization in enhancing ductility during warm deformation. ? 2021 Elsevier B.V. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85098892339&doi=10.1016%2fj.msea.2020.140704&partnerID=40&md5=01274353adcbf52605ba9eab09361d7f https://scholars.lib.ntu.edu.tw/handle/123456789/576923 |
ISSN: | 9215093 | DOI: | 10.1016/j.msea.2020.140704 |
Appears in Collections: | 材料科學與工程學系 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.