標題: | Corrosion resistance and electrical contact resistance of a thin permanganate conversion coating on dual-phase LZ91 Mg–Li alloy | 作者: | Hung S.-M Lin H Chen H.-W Chen S.-Y CHAO-SUNG LIN |
關鍵字: | Conversion coating;Electrical contact resistance;Magnesium;Polarization;Transmission electron microscopy;X-ray photon spectroscopy;Contact resistance;Corrosion resistant alloys;Corrosion resistant coatings;High resolution transmission electron microscopy;Lithium alloys;Magnesia;Magnesium alloys;Manganese alloys;Manganese oxide;Potash;Coating solution;Conversion coatings;Dual phase;Dual phasis;Magnesium-lithium alloys;Mg-Li alloy;Resistance contact;Thin protective coatings;X ray photon spectroscopy;Corrosion resistance | 公開日期: | 2021 | 卷: | 11 | 起(迄)頁: | 1953-1968 | 來源出版物: | Journal of Materials Research and Technology | 摘要: | A strongly acidic permanganate conversion coating solution containing 0.1 M KMnO4 at pH 1.5 adjusted with H2SO4 was employed for LZ91 magnesium-lithium alloy, realizing the formation of a thin protective coating with a low electrical contact resistance. The corrosion resistance of LZ91 alloy was markedly improved by the permanganate conversion coating, which consisted of MgO, MnO2, and Mg(OH)2. Coating formation proceeded on both the α-Mg phase and β-Li phase in this strongly acidic permanganate solution, achieving a full coverage of permanganate conversion coating within a short treatment time. When the immersion was prolonged to 30 s, cracks were present on the permanganate conversion coating, which deteriorated the corrosion resistance substantially. Moreover, the increase in the thickness of the coating elevated the electrical contact resistance. However, the relatively thin areas on the thin permanganate conversion coating became active sites where corrosion commenced. As a result, a thin uniform permanganate conversion coating is crucial for both enhanced corrosion resistance and reduced electrical contact resistance. ? 2021 The Author(s) |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85106740318&doi=10.1016%2fj.jmrt.2021.02.050&partnerID=40&md5=b7f566351c4e6c17b7315d92ea21b5c3 https://scholars.lib.ntu.edu.tw/handle/123456789/598339 |
ISSN: | 22387854 | DOI: | 10.1016/j.jmrt.2021.02.050 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。