標題: | Microstructural variation in fatigued interphase arrayed nano-precipitated Ti-microalloyed steel | 作者: | Yen C.-N Chang L.-W Hsu C.-A Yang J.-R Chang H.-Y Wang S.-H Chen H.-R. JER-REN YANG |
關鍵字: | Arrayed interphase nano-precipitates;Fatigue;Misorientation angle;Preferred orientation;TiC;Alloy steel;Fatigue of materials;Ferrite;Grain boundaries;Microalloying;Steel metallography;Strain rate;Titanium alloys;Arrayed interphase nano-precipitate;Cycle number;Fatigue deformation;Ferrite matrix;Microstructural variation;Nanoprecipitate;Preferred orientations;Size and shape;Ti microalloyed steels;Titanium carbide | 公開日期: | 2021 | 卷: | 15 | 起(迄)頁: | 2393-2404 | 來源出版物: | Journal of Materials Research and Technology | 摘要: | In the present study, arrayed nano-precipitated TiC in a ferrite matrix was obtained through thermal treatment. The size and shape of the arrayed interphase nano-precipitates were unaffected by fatigue deformation in this Ti-microalloyed steel. In addition, arrayed arrangement of the interphase nano-precipitates was not disrupted by fatigue and still remained only at low cycle numbers, which corresponded to the shortest fatigue life. The interphase nano-precipitated steel was strengthened through a bowing mechanism through which unpinning occurred, dislocation loops were formed, and the microhardness of ferrite was increased. The development of an incipient cell structure in the ferrite matrix was caused by wavy dislocation. After the onset of fatigue, the grain was preferentially rotated toward the {101}α orientation. Higher strain amplitude or lower strain rate led to a more favorable degree of misorientation in the low-angle grain boundaries. ? 2021 The Author(s) |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85115953721&doi=10.1016%2fj.jmrt.2021.09.054&partnerID=40&md5=41a344a68c4254e75a25548c2caf0ef4 https://scholars.lib.ntu.edu.tw/handle/123456789/598392 |
ISSN: | 22387854 | DOI: | 10.1016/j.jmrt.2021.09.054 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。