標題: | Effects of Grain Size on the Ag Dissolution and Ion Migration of Ag-4Pd Alloy Wires | 作者: | Lin Y.-C Lee P.-I Wu P.-C Chen C.-H Chuang T.-H. TUNG-HAN CHUANG |
關鍵字: | Ag dissolution;Ag ion migration;Ag-4Pd alloy wires;annealing twins;grain refining;Binary alloys;Corrosive effects;Dissolution;Electrodes;Grain refinement;Grain size and shape;Ions;Silicon alloys;Silver alloys;Silver oxides;Thermodynamic stability;Wire;Ag dissolutions;Annealing twins;Coarse grains;Coarse-grained;Corrosion behavior;Electrochemical polarization test;In-situ observations;Passive films;Palladium alloys | 公開日期: | 2021 | 卷: | 50 | 期: | 10 | 起(迄)頁: | 5955-5964 | 來源出版物: | Journal of Electronic Materials | 摘要: | Ion migration and corrosion behavior in Ag-4Pd alloy wires with fine and coarse grains in the outer regions were evaluated with water drop tests. The results from the in situ observations and measurements of Ag ion migration in both Ag-4Pd bonding wires indicated that the fine-grained wire had much shorter times of dendrite contact and short circuit than those of coarse-grained wire for various wire spaces. It was obvious that grain refinement in Ag-4Pd alloy wires accelerated the ion migration of Ag-4Pd alloy wires. Electrochemical polarization tests confirmed that the passive film on fine-grained Ag-4Pd wire was easily broken down, leading to a higher Ag dissolution tendency than that of coarse-grained wire. Although an annealing twin-rich Ag-4Pd alloy wire was shown to enhance the thermal stability of the grain structure and mechanical properties, the large number of twins had no influence on the formation of Ag dendrites on the cathode and Ag2O oxide on the anode of the coarse-grained Ag-4Pd wire couple during ion migration. ? 2021, The Minerals, Metals & Materials Society. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85111561537&doi=10.1007%2fs11664-021-09119-9&partnerID=40&md5=758f7a41c4b93cbdc608309b9e82e8f2 https://scholars.lib.ntu.edu.tw/handle/123456789/598470 |
ISSN: | 03615235 | DOI: | 10.1007/s11664-021-09119-9 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。