標題: | Electronic and bonding structures of amorphous Si-C-N thin films by x-ray absorption spectroscopy | 作者: | Tsai H.M. Chen L.C. LI-CHYONG CHEN |
公開日期: | 2001 | 卷: | 79 | 期: | 15 | 起(迄)頁: | 2393-2395 | 來源出版物: | Applied Physics Letters | 摘要: | X-ray absorption near edge structure (XANES) spectra of hard amorphous a-Si-C-N thin films with various compositions were measured at the C and N K-edge using sample drain current and fluorescent modes. The C K-edge XANES spectra of a-Si-C-N contain a relatively large 1s → π* peak, indicating that a substantial percentage of carbon atoms in the a-Si-C-N films have sp2 or graphite-like bonding. Both the observed sp2 intensity and the Young's modulus decrease with an increase in the carbon content. For N K-edge XANES spectra of the a-Si-C-N films we find the emergence of a sharp peak near the threshold when the carbon content is larger than between 9% and 36%, which indicates that carbon and nitrogen atoms tend to form local graphitic carbon nitride. © 2001 American Institute of Physics. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-0040330136&doi=10.1063%2f1.1409275&partnerID=40&md5=04a21c94a3a0734862a04940fff714e1 https://scholars.lib.ntu.edu.tw/handle/123456789/616414 |
ISSN: | 00036951 | DOI: | 10.1063/1.1409275 |
顯示於: | 凝態科學研究中心 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。