標題: | Characteristics of particleboard made from recycled wood-waste chips impregnated with phenol formaldehyde resin | 作者: | Yang T.-H Lin C.-J Wang S.-Y MING-JER TSAI |
關鍵字: | Bending strength; Internal bonding strength; Retention rate of bending strength; Thickness swelling; Ultrasonic wave velocity | 公開日期: | 2007 | 卷: | 42 | 期: | 1 | 起(迄)頁: | 189-195 | 來源出版物: | Building and Environment | 摘要: | The main purpose of this study was to manufacture water-resistant particleboard for use in kitchens and bathrooms, and as flooring-based material and in outdoor environments. The chips were from recycled wood wastes of different wood species. The chips were divided into coarse chips with dimensions of 5-8 mesh and fine chips of 8-20 mesh, then, these chips were immersed in water-soluble phenol formaldehyde (PF) resin solution at concentrations of 4.5%, 6.5% and 10%. After 5 min, they were removed from the PF solution and dried in an oven until in a half-hardened condition. Three-layer mats with target densities of 0.70 and 0.80 g/cm3 were formed by using fine chips for the face layer (25%) and back layer (25%) and coarse chips for the core layer (50%). A conventional hot press was used for fabrication of the particleboard, and the temperature, pressure and pressing time were 453 K, 2.9 MPa, and 5 min, respectively. The nominal dimensions of particleboard were 500×500×12 mm (thick). Result showed that the PF resin absorption content of chips (RC) increased linearly with an increase in the concentration of PF solution. Their relationship could be represented by the linear regression formula. The bending strength, internal bonding strength, and thickness swelling (%) of the PF-impregnated particleboards exhibited excellent performances compared to those made in the past, and the retention rate (%) of the modulus of rupture (MOR) and modulus of elasticity (MOE) of PF-impregnated particleboard after treatment in hot water (343 K) for 2 h were maintained at 48.7-84.5% and 49.2-82.7%, respectively. Characteristics of the ultrasonic velocity in the mechanical direction were similar to those in the vertical direction. In addition, there were significant relationships between the ultrasonic velocity and the mechanical properties of the particleboard, and this meant that we could evaluate the properties of the particleboard using ultrasonic velocity. © 2005 Elsevier Ltd. All rights reserved. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-33748885440&doi=10.1016%2fj.buildenv.2005.08.028&partnerID=40&md5=ea6bf661bd178f23dcac09bce2b725f0 https://scholars.lib.ntu.edu.tw/handle/123456789/626021 |
ISSN: | 03601323 | DOI: | 10.1016/j.buildenv.2005.08.028 | SDG/關鍵字: | Bending strength; Bonding; Elastic moduli; Phenolic resins; Ultrasonic velocity; Internal bonding strength; Modulus of rupture (MOR); Phenol formaldehyde (PF) resin solution; Thickness swelling; Particle board; Bending strength; Bonding; Elastic moduli; Particle board; Phenolic resins; Ultrasonic velocity; bending; elastic modulus; formaldehyde; phenol |
顯示於: | 森林環境暨資源學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。