標題: | Properties of low-formaldehyde-emission particleboard made from recycled wood-waste chips sprayed with PMDI/PF resin | 作者: | Wang S.-Y Yang T.-H Lin L.-T Lin C.-J MING-JER TSAI |
關鍵字: | Internal bonding strength; Particleboard; Phenol-formaldehyde resin; Polymeric 4, 4′-methylenediphenyl isocyanate (PMDI); Quantity of formaldehyde released; Thickness swelling | 公開日期: | 2007 | 卷: | 42 | 期: | 7 | 起(迄)頁: | 2472-2479 | 來源出版物: | Building and Environment | 摘要: | The objective of this study was to manufacture low-formaldehyde-emission particleboard from recycled wood-waste chips using polymeric 4,4′-methylenediphenyl isocyanate (PMDI) and phenol-formaldehyde (PF) resins for use in indoor environments. The influence of PMDI/PF ratios in particles on the formaldehyde emission and its mechanical properties were investigated. The experimental results showed that the formaldehyde emission released decreased linearly with increasing PMDI/PF particle ratio. The relationship could be represented by a linear regression formula. Formaldehyde emission was below 0.3 mg/L when the weight percentage of PMDI/particles was up to 70%. The formaldehyde emission from melamine-formaldehyde (MF) resin-impregnated paper-overlaid particleboard was 17% lower than that for particleboard. Moreover, the bending strength, internal bonding strength and screw holding strength increased with increasing PMDI/PF particle ratio. However, the percentage thickness swelling of the particleboard decreased with increasing PMDI/PF particle ratio. In addition, there were significant positive relationships between the ultrasonic velocity and the bending strength, internal bonding strength and screw holding strength of the particleboard, which allowed evaluation of the properties of the particleboard using ultrasonic velocity. © 2006 Elsevier Ltd. All rights reserved. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-33847032598&doi=10.1016%2fj.buildenv.2006.06.009&partnerID=40&md5=80d91dfdd198e27e4c68c77bd30f812a https://scholars.lib.ntu.edu.tw/handle/123456789/626138 |
ISSN: | 03601323 | DOI: | 10.1016/j.buildenv.2006.06.009 | SDG/關鍵字: | Bending strength; Formaldehyde; Linear regression; Phenolic resins; Swelling; Ultrasonic velocity; Wood wastes; Low-formaldehyde-emission particleboard; Phenol-formaldehyde; Particle board; Bending strength; Formaldehyde; Linear regression; Particle board; Phenolic resins; Swelling; Ultrasonic velocity; Wood wastes; experimental study; formaldehyde; mechanical property; regression analysis; swelling; wood; Bend Strength; Formaldehyde; Particle Boards; Polyphenolics; Swelling; Ultrasonic Frequencies; Wood Waste |
顯示於: | 森林環境暨資源學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。