Wide Range pH-Tolerable Silicon@Pyrite Cobalt Dichalcogenide Microwire Array Photoelectrodes for Solar Hydrogen Evolution

Journal
ACS applied materials & interfaces
Journal Volume
8
Journal Issue
8
Date Issued
2016-03-02
Author(s)
CHIH-JUNG CHEN  
Yang, Kai-Chih
Basu, Mrinmoyee
Lu, Tzu-Hsiang
Lu, Ying-Rui
Dong, Chung-Li
Hu, Shu-Fen
Liu, Ru-Shi
DOI
10.1021/acsami.6b00027
URI
https://scholars.lib.ntu.edu.tw/handle/123456789/628175
URL
https://api.elsevier.com/content/abstract/scopus_id/84959507872
Abstract
This study employed silicon@cobalt dichalcogenide microwires (MWs) as wide range pH-tolerable photocathode material for solar water splitting. Silicon microwire arrays were fabricated through lithography and dry etching technologies. Si@Co(OH)2 MWs were utilized as precursors to synthesize Si@CoX2 (X = S or Se) photocathodes. Si@CoS2 and Si@CoSe2 MWs were subsequently prepared by thermal sulfidation and hydrothermal selenization reaction of Si@Co(OH)2, respectively. The CoX2 outer shell served as cocatalyst to accelerate the kinetics of photogenerated electrons from the underlying Si MWs and reduce the recombination. Moreover, the CoX2 layer completely deposited on the Si surface functioned as a passivation layer by decreasing the oxide formation on Si MWs during solar hydrogen evolution. Si@CoS2 photocathode showed a photocurrent density of -3.22 mA cm(-2) at 0 V (vs RHE) in 0.5 M sulfuric acid electrolyte, and Si@CoSe2 MWs revealed moderate photocurrent density of -2.55 mA cm(-2). However, Si@CoSe2 presented high charge transfer efficiency in neutral and alkaline electrolytes. Continuous chronoamperometry in acid, neutral, and alkaline solutions was conducted at 0 V (vs RHE) to evaluate the photoelectrochemical durability of Si@CoX2 MWs. Si@CoS2 electrode showed no photoresponse after the chronoamperometry test because it was etched through the electrolyte. By contrast, the photocurrent density of Si@CoSe2 MWs gradually increased to -5 mA cm(-2) after chronoamperometry characterization owing to the amorphous structure generation.
Subjects
co-catalyst; cobalt dichalcogenide; hydrogen evolution; silicon microwire arrays; solar water splitting; wide range pH toleration
Type
journal article

臺大位居世界頂尖大學之列,為永久珍藏及向國際展現本校豐碩的研究成果及學術能量,圖書館整合機構典藏(NTUR)與學術庫(AH)不同功能平台,成為臺大學術典藏NTU scholars。期能整合研究能量、促進交流合作、保存學術產出、推廣研究成果。

To permanently archive and promote researcher profiles and scholarly works, Library integrates the services of “NTU Repository” with “Academic Hub” to form NTU Scholars.

總館學科館員 (Main Library)
醫學圖書館學科館員 (Medical Library)
社會科學院辜振甫紀念圖書館學科館員 (Social Sciences Library)

開放取用是從使用者角度提升資訊取用性的社會運動,應用在學術研究上是透過將研究著作公開供使用者自由取閱,以促進學術傳播及因應期刊訂購費用逐年攀升。同時可加速研究發展、提升研究影響力,NTU Scholars即為本校的開放取用典藏(OA Archive)平台。(點選深入了解OA)

  • 請確認所上傳的全文是原創的內容,若該文件包含部分內容的版權非匯入者所有,或由第三方贊助與合作完成,請確認該版權所有者及第三方同意提供此授權。
    Please represent that the submission is your original work, and that you have the right to grant the rights to upload.
  • 若欲上傳已出版的全文電子檔,可使用Open policy finder網站查詢,以確認出版單位之版權政策。
    Please use Open policy finder to find a summary of permissions that are normally given as part of each publisher's copyright transfer agreement.
  • 網站簡介 (Quickstart Guide)
  • 使用手冊 (Instruction Manual)
  • 線上預約服務 (Booking Service)
  • 方案一:臺灣大學計算機中心帳號登入
    (With C&INC Email Account)
  • 方案二:ORCID帳號登入 (With ORCID)
  • 方案一:定期更新ORCID者,以ID匯入 (Search for identifier (ORCID))
  • 方案二:自行建檔 (Default mode Submission)
  • 方案三:學科館員協助匯入 (Email worklist to subject librarians)

Built with DSpace-CRIS software - Extension maintained and optimized by 4Science