https://scholars.lib.ntu.edu.tw/handle/123456789/630150
標題: | Highly compressible hydrogel reinforced with cellulose nanocrystals for ultrasound scanning via microwave-assisted synthesis | 作者: | Cheng, Der Yun Liao, I. Hsiang JIASHING YU YING-CHIH LIAO |
關鍵字: | Cellulose nanocrystal | Microwave | PAA hydrogel | Ultrasound transmitting | 公開日期: | 1-十二月-2022 | 出版社: | SPRINGER | 卷: | 29 | 期: | 18 | 起(迄)頁: | 9791 | 來源出版物: | Cellulose | 摘要: | In this study, a rapid fabrication method was developed to prepare hydrogel structures with high mechanical strength and low attenuation coefficient for ultrasound scanning. Poly acrylic acid (PAA) hydrogel was first prepared via a free radical polymerization approach. To shorten the process time (~ 30 min in water bath), microwave heating was applied to facilitate the reaction and reduce the reaction time down to 80 s. The produced hydrogels showed excellent elasticity but had a low compressive strength of 100 kPa. To further enhance the mechanical strengths of PAA hydrogels, cellulosenanocrystals (CNCs) were added to the precursor solution. After the microwave assisted crosslinking process, the compressive strength of the hydrogel increased to 350 kPa. Moreover, the ultimate compressive strain was enhanced from 60 to 80% with great recoverability. The PAA/CNC hydrogel has a great ultrasound trnansimission for high-quality ultrasound images comparable to conventional liquid hydrogels. To demonstrate the feasibility of the PAA/CNC hydrogel in ultrasonic medical applications, a customized ultrasound probe coat was created with a 3D printed mold and practically used in the ultrasound scanning process. Graphical abstract: [Figure not available: see fulltext.]. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/630150 | ISSN: | 09690239 | DOI: | 10.1007/s10570-022-04854-6 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。