標題: | Solid solubility limited dopant activation of group III dopants (B, Ga & In) in Ge targeting sub-7nm node low p+ contact resistance | 作者: | Borland J Lee Y.-J Chuang S.-S Tseng T.-Y CHEE-WEE LIU Huet K Goodman G Marino J. |
公開日期: | 2017 | 起(迄)頁: | 94-97 | 來源出版物: | 17th International Workshop on Junction Technology, IWJT 2017 | 摘要: | Low contact resistance (Rc) is key to boost device performance for sub-10nm node. At VLSI Technology Symposium 2016 Samsung reported they reduced Rc by 10% from 14nm to 10nm bulk FinFET technology [1]. TSMC in their beyond 10nm node FinFET paper reported reducing S/D (source/drain) parasitic resistance and enhanced contact process [2] and at IEDM-2016 reported 7nm FinFET reduced S/D parasitic resistance and developed a novel contact process [3]. A complete session #7 was dedicated to 'Contact Resistance Innovations for Sub 10nm Scaling' with 4 papers at the VLSI Technology Symposium 2016 [4-7]. To achieve Rc in the low E-9 Ωcm2 requires active dopant carrier concentration >5E20/cm3 to low E21/cm3. For SiP n+ S/D contacts P >1E21/cm3 active dopant carrier concentration is realized with laser melt annealing resulting in Rc <1E-9 Ωcm2 [6]. For 70%-SiGe p+ S/D contacts IMEC reported using pre and post Ge amorphous implants to boost the B-implant activation with nsec laser melt annealing to reduce Rc from 1.2E-8 Ωcm2 to 2.1E-9 Ωcm2 [4]. IBM/GF on the other hand reported reducing SiGe p+ S/D Rc from 1.3E-8 Ωcm2 to 1.9E-9 Ωcm2 by using a thin 12nm 100%-Ge trench-epi and switching from a p+ Ge:B to a p+ Ge:B:group-III metastable alloy for surface interface doping [8]. The group-III Me-alloy in Ge boosted p+ dopant activation from ??E19/cm3 with B to ??E20/cm3 with Ge+Me-alloy. They mentioned no difference between msec non-melt and nsec melt laser annealing. © 2017 JSAP. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85026737894&doi=10.23919%2fIWJT.2017.7966526&partnerID=40&md5=1b9a5fa037ea7b449968db01a4d61e29 https://scholars.lib.ntu.edu.tw/handle/123456789/632197 |
DOI: | 10.23919/IWJT.2017.7966526 | SDG/關鍵字: | Annealing; Carrier concentration; Chemical activation; Contact resistance; Doping (additives); FinFET; Germanium; Nanotechnology; Silicon alloys; VLSI circuits; Contact process; Device performance; Dopant activation; Metastable alloy; Parasitic resistances; Solid solubilities; Surface interfaces; VLSI technology; Si-Ge alloys |
顯示於: | 電機工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。