標題: | Enhanced Cu-to-Cu Bonding by Using Sn Passivation Layer | 作者: | Kung, P. Y. Huang, W. L. Kao, C. L. Hung, Y. C. C. ROBERT KAO |
關鍵字: | 3D IC | Compensate for the height difference | Cu-to-Cu bonding | Sn passivation layer | 公開日期: | 1-一月-2023 | 來源出版物: | 2023 International Conference on Electronics Packaging, ICEP 2023 | 摘要: | This study discusses the advantage of Sn-passivated Cu-to-Cu bonding compared to Cu-to-Cu direct bonding. However, Sn-capped Cu bonding in the semiconductor industry has been studied since 15 years ago, and seldom research indicated that the Sn passivate layer can tolerate surface height difference in the Cu-to-Cu bonding. Moreover, in the previous related study, the Sn layer thickness was thicker than 1.2 μm, and the bonding temperature was higher than 250°C. In this experiment, 1 μm Sn is electroplated over the Cu to compensate for the Cu surface height difference and lower the bonding temperature and pressure. Furthermore, the process was done by thermal compressive bonding (TCB), and two temperatures, 250°C and 220°C, were conducted in the experiment. Furthermore, 1 MPa and 1-minute bonding condition is used in the experiment to meet the low-pressure and high-efficient bonding process. To conclude, by passivating Sn over Cu, severe condition is not required. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/634043 | ISBN: | 9784991191152 | DOI: | 10.23919/ICEP58572.2023.10129779 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。