標題: | Robust and Intimate Interface Enabled by Silicon Carbide as an Additive to Anodes for Lithium Metal Solid-State Batteries | 作者: | Srivastava, Pavitra Liao, Yu-Kai Iputera, Kevin Hu, Shu-Fen RU-SHI LIU |
關鍵字: | Li metal anode; critical current density; garnet electrolytes; interface modification; solid-state batteries | 公開日期: | 28-七月-2023 | 來源出版物: | ChemSusChem | 摘要: | Garnet-type solid-state electrolytes are among the most reassuring candidates for the development of solid-state lithium metal batteries (SSLMB) because of their wide electrochemical stability window and chemical feasibility with lithium. However, issues such as poor physical contact with Li metal tend to limit their practical applications. These problems were addressed using β-SiC as an additive to the Li anode, resulting in improved wettability over Li6.75 La3 Zr1.75 Ta0.25 O12 (LLZTO) and establishing an improved interfacial contact. At the Li-SiC|LLZTO interface, intimacy was induced by a lithiophilic Li4 SiO4 phase, whereas robustness was attained through the hard SiC phase. The optimized Li-SiC|LLZTO|Li-SiC symmetric cell displayed a low interfacial impedance of 10 Ω cm2 and superior cycling stability at varying current densities up to 5800 h. Moreover, the modified interface could achieve a high critical current density of 4.6 mA cm-2 at room temperature and cycling stability of 1000 h at 3.5 mA cm-2 . The use of mechanically superior materials such as SiC as additives for the preparation of a composite anode may serve as a new strategy for robust garnet-based SSLMB. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/634658 | ISSN: | 18645631 | DOI: | 10.1002/cssc.202300504 |
顯示於: | 化學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。