標題: | In Situ and Low-Cost Improvement of the Lithium Anode Interface in Garnet-Type Solid-State Electrolytes | 作者: | Liao, Yu-Kai RU-SHI LIU Yao, Sung-Ting Hu, Shu-Fen |
關鍵字: | Li–Ca–Cl; garnet; in situ; lithiumphilic; low-cost; solid-state Li metal battery | 公開日期: | 28-十一月-2023 | 卷: | 15 | 期: | 49 | 起(迄)頁: | 57828 | 來源出版物: | ACS applied materials & interfaces | 摘要: | In recent years, the development of electric vehicles and environmental concerns have made necessary improvements in the energy density and safety of lithium-ion batteries. Therefore, the development of all-solid-state lithium-ion batteries (ASSLIBs) has become imperative. One advantage of ASSLIBs is their potential for downsizing with the use of lithium metal as the anode. However, in this study, a garnet-type solid electrolyte (Li6.75La3Zr1.75Ta0.25O12) was used, which has low reactivity with lithium metal. Thus, interface modification using CaCl2 was employed to form a Li-Ca-Cl composite anode. The interfacial resistance was remarkably reduced to 7 Ω cm2, and the symmetric cell exhibited stable cycling for 1200 h at room temperature and a current density of 0.1 mA cm-2. The voltage ranged from ±15 to ±16 mV. The full cell demonstrated a high initial discharge capacity of 149.2 mA h g-1 and a Coulombic efficiency of 98.0% while maintaining a discharge capacity retention of 91.3% after 100 cycles. These findings lay a solid foundation for future commercial applications as interface modification was achieved through a simple spin-coating process using low-cost CaCl2 (0.7 USD g-1). |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/638487 | ISSN: | 19448244 | DOI: | 10.1021/acsami.3c13222 |
顯示於: | 化學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。